ISO	Workpiece material	Grade	Shape	Cutting speed Vc (m/min)	Feed per tooth fz (mm/t)
	Grey cast iron FC250, etc. , 250, etc.	BX480	2-SWGW130508PDLSR	800 – 1500	0.05 – 0.3

TAW / EAW 13 type

Roughing (Depth of cut: ap ≥ 1.0 mm)

ISO	Workpiece material	Grade	Chip-breaker	Cutting speed Vc (m/min)	Feed per tooth fz (mm/t)
	Mild steels, Low carbon steels (< 180HB)	AH120 (First choice)	MJ	180 (100 – 270)	0.2 (0.05 – 0.3)
		AH120 (First choice)	ML	180 (100 – 270)	0.15 (0.05 – 0.25)
		AH120 (First choice)	HJ	180 (100 – 270)	0.4 (0.2 – 0.6)
		AH120 (First choice)	Flat top	180 (100 – 270)	0.2 (0.05 – 0.3)
		T3130 (Priority on wear resistance)	MJ	220 (150 – 300)	0.2 (0.05 – 0.3)
		T3130 (Priority on wear resistance)	HJ	220 (150 – 300)	0.4 (0.2 – 0.6)
		T3130 (Priority on wear resistance)	Flat top	220 (150 – 300)	0.2 (0.05 – 0.3)
		AH130 / AH140 (Priority on impact resistance)	MJ	130 (80 – 180)	0.2 (0.05 – 0.3)
		AH130 / AH140 (Priority on impact resistance)	MS	130 (80 – 180)	0.17 (0.1 – 0.25)
		NS740 (Priority on surface fi nish)	MJ	200 (100 – 300)	0.15 (0.05 – 0.23)
		NS740 (Priority on surface fi nish)	Flat top	200 (100 – 300)	0.15 (0.05 – 0.23)
	Carbon steels, Alloy steels (< 300HB)	AH120 (First choice)	MJ	150 (100 – 230)	0.17 (0.05 – 0.25)
		AH120 (First choice)	ML	150 (100 – 230)	0.12 (0.05 – 0.2)
		AH120 (First choice)	HJ	150 (100 – 230)	0.3 (0.2 – 0.5)
		AH120 (First choice)	Flat top	150 (100 – 230)	0.17 (0.05 – 0.25)
		T3130 (Priority on wear resistance)	MJ	200 (150 – 280)	0.17 (0.05 – 0.25)
		T3130 (Priority on wear resistance)	HJ	200 (150 – 280)	0.3 (0.2 – 0.5)
		T3130 (Priority on wear resistance)	Flat top	200 (150 – 280)	0.17 (0.05 – 0.25)
		AH130 / AH140 (Priority on impact resistance)	MJ	120 (80 – 150)	0.17 (0.05 – 0.25)
		AH130 / AH140 (Priority on impact resistance)	HJ	120 (80 – 150)	0.3 (0.2 – 0.5)
		NS740 (Priority on surface fi nish)	MJ	150 (100 – 230)	0.12 (0.05 – 0.2)
		NS740 (Priority on surface fi nish)	Flat top	150 (100 – 230)	0.12 (0.05 – 0.2)
	Die steels (< 30HRC)	AH120 (First choice)	MJ	140 (100 – 180)	0.12 (0.05 – 0.2)
		AH120 (First choice)	ML	140 (100 – 180)	0.12 (0.05 – 0.2)
		AH120 (First choice)	HJ	140 (100 – 180)	0.3 (0.2 – 0.4)
		AH120 (First choice)	Flat top	140 (100 – 180)	0.12 (0.05 – 0.2)
		T3130 (Priority on wear resistance)	MJ	140 (100 – 180)	0.12 (0.05 – 0.2)
		T3130 (Priority on wear resistance)	HJ	140 (100 – 180)	0.3 (0.2 – 0.4)
		T3130 (Priority on wear resistance)	Flat top	140 (100 – 180)	0.12 (0.05 – 0.2)
	Stainless steel (< 250HB)	AH130 / AH140 (First choice)	MJ	150 (80 – 200)	0.17 (0.1 – 0.25)
		AH130 / AH140 (First choice)	HJ	150 (80 – 200)	0.3 (0.2 – 0.5)
		AH130 / AH140 (First choice)	MS	150 (80 – 200)	0.15 (0.1 – 0.2)
		AH120 (Priority on wear resistance)	MJ	200 (150 – 250)	0.17 (0.1 – 0.25)
		AH120 (Priority on wear resistance)	ML	200 (150 – 250)	0.15 (0.1 – 0.2)
		AH120 (Priority on wear resistance)	HJ	200 (150 – 250)	0.3 (0.2 – 0.5)
		AH120 (Priority on wear resistance)	Flat top	200 (150 – 250)	0.17 (0.1 – 0.25)
	Grey castirons, Ductile cast irons	T1115 (First choice)	MJ	180 (100 – 250)	0.17 (0.05 – 0.25)
		T1115 (First choice)	HJ	180 (100 – 250)	0.4 (0.2 – 0.6)
		T1115 (First choice)	Flat top	180 (100 – 250)	0.17 (0.05 – 0.25)
		AH120 (Priority on impact resistance)	MJ	180 (100 – 250)	0.17 (0.05 – 0.25)
		AH120 (Priority on impact resistance)	ML	180 (100 – 250)	0.15 (0.05 – 0.2)
		AH120 (Priority on impact resistance)	HJ	180 (100 – 250)	0.4 (0.2 – 0.6)
		AH120 (Priority on impact resistance)	Flat top	180 (100 – 250)	0.17 (0.05 – 0.25)
	Aluminium alloys (Si < 13 %)	DS1100 / KS05F (First choice)	AJ	500 (300 – 1000)	0.12 (0.05 – 0.2)
	Aluminium alloys (Si ≥ 13 %)	DS1100 / KS05F (First choice)	AJ	200 (80 – 300)	0.12 (0.05 – 0.2)
	Copper alloys	DS1100 / KS05F (First choice)	AJ	350 (200 – 500)	0.12 (0.05 – 0.2)

TAW / EAW 13 type

Light cutting to finishing (Depth of cut: ap ≥ 1.0 mm)

ISO	Workpiece material	Grade	Chip-breaker	Cutting speed Vc (m/min)	Feed per tooth fz (mm/t)
	Mild steels, Low carbon steels (< 180HB)	AH120 (First choice)	MJ	180 (100 – 270)	0.17 (0.05 – 0.25)
		AH120 (First choice)	ML	180 (100 – 270)	0.12 (0.05 – 0.2)
		AH120 (First choice)	HJ	180 (100 – 270)	0.4 (0.2 – 0.6)
		AH120 (First choice)	Flat top	180 (100 – 270)	0.17 (0.05 – 0.25)
		T3130 (Priority on wear resistance)	MJ	220 (150 – 300)	0.17 (0.05 – 0.25)
		T3130 (Priority on wear resistance)	HJ	220 (150 – 300)	0.4 (0.2 – 0.6)
		T3130 (Priority on wear resistance)	Flat top	220 (150 – 300)	0.17 (0.05 – 0.25)
		AH130 / AH140 (Priority on impact resistance)	MJ	130 (80 – 180)	0.17 (0.05 – 0.25)
		AH130 / AH140 (Priority on impact resistance)	MS	130 (80 – 180)	0.15 (0.1 – 0.2)
		NS740 (Priority on surface fi nish)	MJ	200 (100 – 300)	0.12 (0.05 – 0.2)
		NS740 (Priority on surface fi nish)	Flat top	200 (100 – 300)	0.12 (0.05 – 0.2)
	Carbon steels, Alloy steels (< 300HB)	AH120 (First choice)	MJ	150 (100 – 230)	0.12 (0.05 – 0.2)
		AH120 (First choice)	ML	150 (100 – 230)	0.1 (0.05 – 0.15)
		AH120 (First choice)	HJ	150 (100 – 230)	0.3 (0.2 – 0.5)
		AH120 (First choice)	Flat top	150 (100 – 230)	0.12 (0.05 – 0.2)
		T3130 (Priority on wear resistance)	MJ	200 (150 – 280)	0.12 (0.05 – 0.2)
		T3130 (Priority on wear resistance)	HJ	200 (150 – 280)	0.3 (0.2 – 0.5)
		T3130 (Priority on wear resistance)	Flat top	200 (150 – 280)	0.12 (0.05 – 0.2)
		AH130 / AH140 (Priority on impact resistance)	MJ	120 (80 – 150)	0.12 (0.05 – 0.2)
		AH130 / AH140 (Priority on impact resistance)	HJ	120 (80 – 150)	0.3 (0.2 – 0.5)
		NS740 (Priority on surface fi nish)	MJ	150 (100 – 230)	0.12 (0.05 – 0.18)
		NS740 (Priority on surface fi nish)	Flat top	150 (100 – 230)	0.12 (0.05 – 0.18)
	Die steels (< 30HRC)	AH120 (First choice)	MJ	140 (100 – 180)	0.12 (0.05 – 0.18)
		AH120 (First choice)	ML	140 (100 – 180)	0.1 (0.05 – 0.12)
		AH120 (First choice)	HJ	140 (100 – 180)	0.3 (0.2 – 0.4)
		AH120 (First choice)	Flat top	140 (100 – 180)	0.12 (0.05 – 0.18)
		T3130 (Priority on wear resistance)	MJ	140 (100 – 180)	0.12 (0.05 – 0.18)
		T3130 (Priority on wear resistance)	HJ	140 (100 – 180)	0.3 (0.2 – 0.4)
		T3130 (Priority on wear resistance)	Flat top	140 (100 – 180)	0.12 (0.05 – 0.18)
	Stainless steel (< 250HB)	AH130 / AH140 (First choice)	MJ	150 (80 – 200)	0.15 (0.1 – 0.2)
		AH130 / AH140 (First choice)	HJ	150 (80 – 200)	0.3 (0.2 – 0.5)
		AH130 / AH140 (First choice)	MS	150 (80 – 200)	0.15 (0.1 – 0.18)
		AH120 (Priority on wear resistance)	MJ	200 (150 – 250)	0.15 (0.1 – 0.2)
		AH120 (Priority on wear resistance)	ML	200 (150 – 250)	0.15 (0.1 – 0.18)
		AH120 (Priority on wear resistance)	HJ	200 (150 – 250)	0.3 (0.2 – 0.5)
		AH120 (Priority on wear resistance)	Flat top	200 (150 – 250)	0.15 (0.1 – 0.2)
	Grey castirons, Ductile cast irons	T1115 (First choice)	MJ	180 (100 – 250)	0.15 (0.05 – 0.2)
		T1115 (First choice)	HJ	180 (100 – 250)	0.4 (0.2 – 0.6)
		T1115 (First choice)	Flat top	180 (100 – 250)	0.15 (0.05 – 0.2)
		AH120 (Priority on impact resistance)	MJ	180 (100 – 250)	0.15 (0.05 – 0.2)
		AH120 (Priority on impact resistance)	ML	180 (100 – 250)	0.12 (0.05 – 0.18)
		AH120 (Priority on impact resistance)	HJ	180 (100 – 250)	0.4 (0.2 – 0.6)
		AH120 (Priority on impact resistance)	Flat top	180 (100 – 250)	0.15 (0.05 – 0.2)
	Aluminium alloys (Si < 13 %)	DS1100 / KS05F (First choice)	AJ	500 (300 – 1000)	0.12 (0.05 – 0.2)
	Aluminium alloys (Si ≥ 13 %)	DS1100 / KS05F (First choice)	AJ	200 (80 – 300)	0.12 (0.05 – 0.2)
	Copper alloys	DS1100 / KS05F (First choice)	AJ	350 (200 – 500)	0.12 (0.05 – 0.2)

TPW / EPW 13 type

Roughing (Depth of cut: ap ≥ 1.0 mm)

ISO	Workpiece material	Grade	Chip-breaker	Cutting speed Vc (m/min)	Feed per tooth fz (mm/t)
	Mild steels, Low carbon steels (< 180HB)	AH120 (First choice)	MJ	180 (100 – 270)	0.17 (0.05 – 0.25)
		AH120 (First choice)	ML	180 (100 – 270)	0.12 (0.05 – 0.2)
		T3130 (Priority on wear resistance)	MJ	220 (150 – 300)	0.17 (0.05 – 0.25)
		AH130 / AH140 (Priority on impact resistance)	MJ	130 (80 – 180)	0.17 (0.05 – 0.25)
		AH130 / AH140 (Priority on impact resistance)	MS	130 (80 – 180)	0.12 (0.05 – 0.2)
		NS740 (Priority on surface fi nish)	MJ	150 (100 – 230)	0.1 (0.05 – 0.15)
	Carbon steels, Alloy steels (< 300HB)	AH120 (First choice)	MJ	150 (100 – 230)	0.15 (0.05 – 0.2)
		AH120 (First choice)	ML	150 (100 – 230)	0.1 (0.05 – 0.15)
		T3130 (Priority on wear resistance)	MJ	200 (150 – 280)	0.15 (0.05 – 0.2)
		AH130 / AH140 (Priority on impact resistance)	MJ	120 (80 – 150)	0.15 (0.05 – 0.2)
		NS740 (Priority on surface fi nish)	MJ	200 (150 – 230)	0.1 (0.05 – 0.15)
	Die steels (< 30HRC)	AH120 (First choice)	MJ	140 (100 – 180)	0.1 (0.05 – 0.15)
		AH120 (First choice)	ML	140 (100 – 180)	0.08 (0.05 – 0.12)
		T3130 (Priority on wear resistance)	MJ	140 (100 – 180)	0.1 (0.05 – 0.15)
	Stainless steel (< 250HB)	AH130 / AH140 (First choice)	MJ	150 (80 – 200)	0.15 (0.05 – 0.2)
		AH130 / AH140 (First choice)	MS	150 (80 – 200)	0.12 (0.05 – 0.18)
		AH120 (Priority on wear resistance)	MJ	200 (150 – 250)	0.15 (0.05 – 0.2)
		AH120 (Priority on wear resistance)	ML	200 (150 – 250)	0.1 (0.05 – 0.15)
	Grey castirons, Ductile cast irons	T1115 (First choice)	MJ	180 (100 – 250)	0.15 (0.05 – 0.2)
		AH120 (Priority on impact resistance)	MJ	180 (100 – 250)	0.15 (0.05 – 0.2)
		AH120 (Priority on impact resistance)	ML	180 (100 – 250)	0.1 (0.05 – 0.15)
	Aluminium alloys (Si < 13 %)	DS1100 / KS05F (First choice)	AJ	500 (300 – 1000)	0.15 (0.05 – 0.2)
	Aluminium alloys (Si ≥ 13 %)	DS1100 / KS05F (First choice)	AJ	200 (80 – 300)	0.15 (0.05 – 0.2)
	Copper alloys	DS1100 / KS05F (First choice)	AJ	350 (200 – 500)	0.15 (0.05 – 0.2)

TPW / EPW 13 type

Light cutting to finishing (Depth of cut: ap ≥ 1.0 mm)

ISO	Workpiece material	Grade	Chip-breaker	Cutting speed Vc (m/min)	Feed per tooth fz (mm/t)
	Mild steels, Low carbon steels (< 180HB)	AH120 (First choice)	MJ	180 (100 – 270)	0.15 (0.05 – 0.2)
		AH120 (First choice)	ML	180 (100 – 270)	0.12 (0.05 – 0.18)
		T3130 (Priority on wear resistance)	MJ	220 (150 – 300)	0.15 (0.05 – 0.2)
		AH130 / AH140 (Priority on impact resistance)	MJ	130 (80 – 180)	0.15 (0.05 – 0.2)
		AH130 / AH140 (Priority on impact resistance)	MS	130 (80 – 180)	0.12 (0.05 – 0.18)
		NS740 (Priority on surface fi nish)	MJ	200 (100 – 300)	0.1 (0.05 – 0.12)
	Carbon steels, Alloy steels (< 300HB)	AH120 (First choice)	MJ	150 (100 – 230)	0.12 (0.05 – 0.18)
		AH120 (First choice)	ML	150 (100 – 230)	0.1 (0.05 – 0.12)
		T3130 (Priority on wear resistance)	MJ	200 (150 – 280)	0.12 (0.05 – 0.18)
		AH130 / AH140 (Priority on impact resistance)	MJ	120 (80 – 150)	0.12 (0.05 – 0.18)
		NS740 (Priority on surface fi nish)	MJ	150 (100 – 230)	0.08 (0.05 – 0.12)
	Die steels (< 30HRC)	AH120 (First choice)	MJ	140 (100 – 180)	0.08 (0.05 – 0.12)
		AH120 (First choice)	ML	140 (100 – 180)	0.08 (0.05 – 0.1)
		T3130 (Priority on wear resistance)	MJ	140 (100 – 180)	0.08 (0.05 – 0.12)
	Stainless steel (< 250HB)	AH130 / AH140 (First choice)	MJ	150 (80 – 200)	0.12 (0.05 – 0.18)
		AH130 / AH140 (First choice)	MS	150 (80 – 200)	0.12 (0.05 – 0.15)
		AH120 (Priority on wear resistance)	MJ	200 (150 – 250)	0.12 (0.05 – 0.18)
		AH120 (Priority on wear resistance)	ML	200 (150 – 250)	0.08 (0.05 – 0.12)
	Grey castirons, Ductile cast irons	T1115 (First choice)	MJ	180 (100 – 250)	0.12 (0.05 – 0.18)
		AH120 (Priority on impact resistance)	MJ	180 (100 – 250)	0.12 (0.05 – 0.18)
		AH120 (Priority on impact resistance)	ML	180 (100 – 250)	0.08 (0.05 – 0.12)
	Aluminium alloys (Si < 13 %)	DS1100 / KS05F (First choice)	AJ	500 (300 – 1000)	0.15 (0.05 – 0.2)
	Aluminium alloys (Si ≥ 13 %)	DS1100 / KS05F (First choice)	AJ	200 (80 – 300)	0.15 (0.05 – 0.2)
	Copper alloys	DS1100 / KS05F (First choice)	AJ	350 (200 – 500)	0.15 (0.05 – 0.2)

For more information about this product, visit our online e-catalog or download the product report:

e-Catalog

TAW / EAW

Metric | Imperial

TPW / EPW

Metric | Imperial

PDF

Metric

Main product report_No. 358-G
- Expansion CBN insert No. 358S1-G

Imperial

Main product report_No. 358-US
- Expansion CBN insert No. 358S1-US

BACK

Online-shop

Online-shop
Bestel en vind alles in de online-shop

Kom meer te weten

Elektronische catalogus

Elektronische catalogus
Download CAD tekeningen en 3d modelen

Part:	Cylinder block
Material:	FC250 / 250
Cutter:	TPW13R125M38.1-08 (DCX = 125 mm, CICT = 8)
Insert:	2-SWGW130508PDLSR x6, WSGW130508PDLSR x2
Grade:	BX480
Cutting conditions:	Vc = 800 (m/min) fz = 0.11 (mm/t) Vf = 1,760 (mm/min) ap = 0.2 (mm) ae = ~ 80 (mm) Application: Face milling Coolant: Dry Machine: Horizontal M/C, KM100

Part:	Cylinder block
Material:	FC250 / 250
Cutter:	TPW13 cutter (customized, DCX = 250 mm, CICT = 12)
Insert:	2-SWGW130508PDLSR x10, WSGW130508PDLSR x2
Grade:	BX480
Cutting conditions:	Vc = 1,178 ~ 1,257 (m/min) fz = 0.05 ~ 0.11 (mm/t) Vf = 900 ~ 1,980 (mm/min) ap = 0.2 (mm) ae = ~ 200 (mm) Application: Face milling Coolant: Dry Machine: Horizontal M/C, KM100

Part:	Hydraulic part
Material:	Chromium molybdenum steel (SCM415)
Cutter:	TPW13R080M25.4-04 (ø80, z=4)
Insert:	SWMT1304PDPR-MS
Grade:	AH140
Cutting conditions:	Vc = 120 (m/min) fz = 0.18 (mm/t) Vf = 350 (mm/min) ap = 1.2 (mm) ae = ~ 50 (mm) Application: Face milling Coolant: Dry Machine: –

TAW / EAW, TPW / EPW

The best solution for steel and cast iron milling

Applications & Features

Applications

Features

1. CBN grade inserts for high-speed cast iron machining

Inserts & Grades

Inserts

F2-SWGW

WSGW

SW*T1304

SW**13T3

WWCW13T3AF*R

Grades

BX480

AH130

AH3135

Cutter bodies

Shank Type

EAW13 (ø25 – ø80mm)

Bore Type

TAW13 (ø50 – ø200mm)

Shank Type

EPW13 (ø32 – ø80mm)

Bore Type

TPW13 (ø50 – ø200mm)

Practical examples

Example #1

Example #2

Example #3

Standard cutting conditions

TPW / EPW 13 type

TAW / EAW 13 type

Roughing (Depth of cut: ap ≥ 1.0 mm)

TAW / EAW 13 type

Light cutting to finishing (Depth of cut: ap ≥ 1.0 mm)

TPW / EPW 13 type

Roughing (Depth of cut: ap ≥ 1.0 mm)

TPW / EPW 13 type

Light cutting to finishing (Depth of cut: ap ≥ 1.0 mm)

e-Catalog

TAW / EAW

TPW / EPW

PDF

Metric

Imperial

Search

Related News

Tungaloy Adds CBN Inserts for Cast Iron Finishing to “TPW / EPW Type” Milling Cutter Series

Online-shop

Kom meer te weten

Elektronische catalogus

Kom meer te weten

Bronnen

SNS – Global

SNS – Tungaloy Benelux b.v.